VLDPE made via Spherilene Process

10Y02 is a hexene HP-LLDPE film resin combines ease of processing with excellent physical properties. This resin is particularly suited for stretch wrapping applications, expecially as core layer in coextruded films, as it shown a very good film strength and stretchability.

HDPE: 10Y02
Features
  • excellent physical properties
  • suited for stretch wrapping applications
  • very good film strength
  • stretchability
Density: 0.91
Applications
  • Cast film grade
  • hexene HP-LLDPE film resin
  • core layer in coextruded films
MFI: 2.2
Additives
  • THERMAL ANOTIOXIDANT

Material properties (This data are typical values and are not to be construed as product specifications)

Resin properties Unit Typical Value ASTM Method
Melt Index (g/10’) 2.2 D 1238
Density (g/ml) 0.9100 D 1505
Film properties @
Dart Impact (g) 180 D 1709
Puncture resistance (N) 17.4 Montel
Elmendorf Tear (g) 150/350 D 1922
Tensile strenght at yield (MPa) 10.0/9.0 D 882
Tensile strenght at break (MPa) 46.5/34.5 D 882
Ultimate elongation (%) 480/880 D 882
2% Secant modulus (MPa) 105/110 D 882
Haze (%) 3.0 D 1003
Gloss 45° - 75 D 2457
@ 23 micron film obtained on Dolci coextr. cast line, extruders 70/120/70 mm, 2000 mm flat die Teme. Profile 205->J 280°C.
Recommended procssing conditions for cast film extrusion
Melt Temperature (°C) 230-290 -
Thickness (micron) 15-50 -