(HM-5010T2N (EX3


(HM-5010T2N (EX3

(HM-5010T2N (EX3

HDPE made via Hostalen Process

HM-5010T2N (PE80) is manufactured by the suspension polymerization of ethylene monomer. The polymerization is generally carried out in a batch process. HM-5010T2N grade is a pressure pipes grade for gas and water transportation. UV stabilization and pigments can be used during process.

HDPE:HM-5010T2N (EX3)
  • Tough and rigid pipe resin
Density: 0.945
  • This grade apply for Gas and water transportation. By use of stabilizers and pigments this grade is applied for piping under uv radiation in gas and liquid transportation.
MFI: 12
  • Antioxidant/Process stabilizer
  • Lubricant (processing aid)/acid scavenger

Material properties (This data are typical values and are not to be construed as product specifications)

Resin Properties Unit Typical Value Test Method
Density g/cm3 0.945 ISO 1183
Melt Index (2.16) g/10 min 12 ISO 1133
Melt Index (5) g/10 min 0.45 ISO 1133
FRR (21.6/5) - 27 -
Molded Properties Unit Typical Value Test Method
Notched Impact @ 23 °C mJ/mm² 12 ISO 179/ 1 eA
Mechanical Properties Unit Typical Value Test Method
Hydrostatic Strength (80 ºC) h (4.0 N/mm²) 1000 ISO 1167

Handellling and Health Safety

sMolten polymers could be injured skin or eye so safety glasses and appropriate gloves are suggested to prevent possible thermal injuries. Also appropriate ventilation is suggested in working by melt polymer. Accumulation of fines or dust particles that are in this grade is not suitable because of explosion hazard probability. So adequated filters and grounding exists at all time are recommended.


Polyethylene products (in pelletised or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet cause a change in the material properties.The Storage area should be dry and preferably don't exceed 50 °C. Under cool, dry, dark conditions Jam Polymers polyolefin resins are expected to maintain the original material and processing properties for at least 18 month. . JPC would not ressponsible about quality diminishing such as color change, bad smell or ets which caused by bad storage conditions. It is better to process PE resin within 6 months after delivery.


Jam Polymers Polyolefin resins are supplied in pllet form packed in 25kg bags. Alternative packaging modes are avalable for selected grades.