LLDPE made via Spherilene Process

32604 is a LLDPE for rotomolding which manufactured by gas phase process. This grade is suitable for all applications which need a good balance among moldability and mechanical properties together with an exceptional stress cracking resistance.

HDPE: LL-32604/UV
  • Exellent ESCR.
Density: 0.952
  • High ESCR rotomolded items Chemical containers.
MFI: 5
  • LL-32604:Thermal Antioxidant
  • LL-32604UV:Thermal Antioxidant/ UV Stabilizer

Material properties (This data are typical values and are not to be construed as product specifications)

Resin Properties Unit Typical Value Test Method
Melt Index g/10 min 4 D1238
Density g/cm³ 0.932 D1505
Physical Properties Unit Typical Value Test Method
Flectural Modulus Mpa 1350 D790
Notched Izod Impact @ 23 °C J/m NB D256/A
E.S.C.R h >1000 D1693

Handellling and Health Safety

sMolten polymers could be injured skin or eye so safety glasses and appropriate gloves are suggested to prevent possible thermal injuries. Also appropriate ventilation is suggested in working by melt polymer. Accumulation of fines or dust particles that are in this grade is not suitable because of explosion hazard probability. So adequated filters and grounding exists at all time are recommended.


Polyethylene products (in pelletised or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet cause a change in the material properties.The Storage area should be dry and preferably don't exceed 50 °C. Under cool, dry, dark conditions Jam Polymers polyolefin resins are expected to maintain the original material and processing properties for at least 18 month. . JPC would not ressponsible about quality diminishing such as color change, bad smell or ets which caused by bad storage conditions. It is better to process PE resin within 6 months after delivery


Jam Polymers Polyolefin resins are supplied in pllet form packed in 25kg bags. Alternative packaging modes are avalable for selected grades.