LL-20516

Loading

LL-20516

LL-20516

LLDPE made via Spherilene Process

20516 is a LLDPE injection molding grade which manufactured by gas phase process. This grade is well suited for application requiring good melt flowability during processign and good flexibility of the final items, like clousures and toys alpplications.

HDPE: LL-20516
Features
  • Good melt flowability and good flexibility of the final items, like clousures.
Density: 0.922
Applications
  • Clousures
  • Toys
MFI: 0.5
Additives
  • Thermal Antioxidant

Material properties (This data are typical values and are not to be construed as product specifications)

Resin Properties Unit Typical Value Test Method
Melt Index g/10 min 16 D1238
Density g/cm³ 0.922 D1505
Thermal Properties Unit Typical Value Test Method
Vicat Softening Point °C 88 D1525
Molded Properties Unit Typical Value Test Method
Flectural Modulus Mpa 430 D790
Vicat Softening Point °C 127 D1525
Tensile Strenght at Yield Mpa 11/10 D638
Tensile Strenght at Break Mpa 40/35 D638
Ultimate Elongation % 600/750 D638
Notched Izod Impact @ 23 °C J/m Not Broken D256/A
Notched Izod Impact @ -50 °C J/m 60 D256/A
H.D.T °C 46 D648

Handellling and Health Safety

sMolten polymers could be injured skin or eye so safety glasses and appropriate gloves are suggested to prevent possible thermal injuries. Also appropriate ventilation is suggested in working by melt polymer. Accumulation of fines or dust particles that are in this grade is not suitable because of explosion hazard probability. So adequated filters and grounding exists at all time are recommended.

Storage

Polyethylene products (in pelletised or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet cause a change in the material properties.The Storage area should be dry and preferably don't exceed 50 °C. Under cool, dry, dark conditions Jam Polymers polyolefin resins are expected to maintain the original material and processing properties for at least 18 month. . JPC would not ressponsible about quality diminishing such as color change, bad smell or ets which caused by bad storage conditions. It is better to process PE resin within 6 months after delivery

packaging

Jam Polymers Polyolefin resins are supplied in pllet form packed in 25kg bags. Alternative packaging modes are avalable for selected grades.