کد محصول: 18

HDPE made via Hostalen Process

HM-5010T2N (EX3) is a pipe grade resin which is manufactured by suspension polymerization of ethylene monomer. HM-5010T2N (EX3) is a bi-model high density polyethylene with 1-Butene as co monomer.

HDPE:HM-5010T2N (EX3)
Features
  • Tough and rigid pipe resin
Density: 0.943-0.947 g/cm3
Applications

    • Pressure pipes, e.g. drinking-water and gas pipes,        waste pipes and sewer pipes, their fittings and             also  sheets (UV stabilization and pigments during           processing)

MFI: 12
Additives
  • Antioxidant/Process stabilizer
  • Lubricant (processing aid)/acid scavenger

Material properties (This data are typical values and are not to be construed as product specifications)

Resin Properties Unit Typical Value Test Method
Density g/cm3 0.945 ISO 1183
Melt Index (2.16) g/10 min 12 ISO 1133
Melt Index (5) g/10 min 0.45 ISO 1133
FRR (21.6/5) - 27 -
Molded Properties Unit Typical Value Test Method
Notched Impact @ 23 °C mJ/mm² 12 ISO 179/ 1 eA
Mechanical Properties Unit Typical Value Test Method
Hydrostatic Strength (80 ºC) h (4.0 N/mm²) 1000 ISO 1167

Handellling and Health Safety

sMolten polymers could be injured skin or eye so safety glasses and appropriate gloves are suggested to prevent possible thermal injuries. Also appropriate ventilation is suggested in working by melt polymer. Accumulation of fines or dust particles that are in this grade is not suitable because of explosion hazard probability. So adequated filters and grounding exists at all time are recommended.

Storage

Polyethylene products (in pelletised or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet cause a change in the material properties.The Storage area should be dry and preferably don't exceed 50 °C. It is advisable to process PE resin within 6 months after delivery . JPC would not ressponsible about quality diminishing such as color change, bad smell or ets which caused by bad storage conditions. It is better to process PE resin within 6 months after delivery.

packaging

Jam Polymers Polyolefin resins are supplied in pllet form packed in 25kg bags. Alternative packaging modes are avalable for selected grades.

 

On compression moulded according to ASTM D1928C Processing Conditions Recommended barrel tempratures range between 190 °C and 280 °C.

Shear-Viscosity @ 190 °C

HM5010t2n

 

🗨The above values were Calculated from data for 100 µm produced on a 75mm Barrnage extruder with 190°C melt temperature using a 2:1 blow ratio and a gap die of 3.0 mm.