HM-9450F (EX5) is blown film grade resin which is manufactured by suspension polymerization of ethylene monomer. HM-9450F (EX5) is a bi-model high density polyethylene with 1-Butene as co monomer

HDPE: HM9450F
Features
  • High molar mass film grade, good
    stiffness and tenacity
Density: : 0.947-0.951 g/cm3
Applications

• For blown films with paperlike quality, sutable for counter bags, carrier bags and wrapping films, excellent processing.

MFI: 190/5: 0.23-0.33
Additives
  • Antioxidant/Process stabilizer
  • Lubricant (processing aid)/acid scavenger

Material properties (This data are typical values and are not to be construed as product specifications)

Test/Composition Unit Typical Value Test Method
Density g/cm3 0.949 ISO 1183
Fish Eye Note note ≤ 3 internal
FRR 21.6/5 - 29 -
MFR 190°/21.6 g/10min 8..0 ISO1133
MFR190°/5 g/10min 0.28 ISO1133
  • Test specimen from compression moulded sheet at 23°C.
  • FRR values are statistical and calculated by dividing MFR values
  • Notch Impact Test specimen from compressed moulded sheet 23°C and The data quoted are average values .

Handling and Health Safety

Molten polymers could be injured skin or eye so safety glasses and appropriate gloves are suggested to prevent possible thermal injuries. Also appropriate ventilation is suggested in working by melt polymer. Accumulation of fines or dust particles that are in this grade is not suitable because of explosion hazard probability. So adequated filters and grounding exists at all time are recommended.

Storage

Polyethylene products (in pelletised or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet cause a change in the material properties.The Storage area should be dry and preferably don't exceed 50 °C. Under cool, dry, dark conditions Jam Polymers polyolefin resins are expected to maintain the original material and processing properties for at least 18 month. JPC would not ressponsible about quality diminishing such as color change, bad smell or ets which caused by bad storage conditions. It is better to process PE resin within 6 months after delivery.

packaging

Jam Polymers Polyolefin resins are supplied in Pellet form packed in 25kg bags. Alternative packaging modes are avalable for selected grades.

HM9450f

 

The above values were Calculated from data for 100 µm produced on a 75mm Barrnage extruder with 190°C melt temperature using a 2:1 blow ratio and a gap die of 3.0 mm.

  • 94505
  • 640.82KB
  • پی دی اف
امتیاز را وارد کنید
نام را وارد کنید
تعداد کاراکتر باقیمانده: 400
نظر خود را وارد کنید