HM CRP 100N (PE100

Loading

HM CRP 100N (PE100

کد محصول: 35

HDPE made via Hostalen Process

HM-CRP100N (PE100) is a natural pipe grade resin which is manufactured by suspension polymerization of ethylen monomer, HM-CRP100N )PE100) is a bi-model high density polyethylene with 1-Butene as co monomer

HDPE: HM CRP 100 Black
Features

• Natural PE100 pipe resin.

Density: : 0.946-0.950 g/cm3
Applications

• Top quality PE100 pressure

• Pipes for gas and water transportaion at higher pressures or with thinner walls as PE80 (UV stabilization and/ or pigments during precessing)

MFI: R 190/5: 0.19-0.25
Additives
  • Antioxidant/Process stabilizer
  • Lubricant (processing aid)/acid scavenger

Material properties (This data are typical values and are not to be construed as product specifications)

Test/Composition Unit Typical Value Test Method
FRR 21.6/5 - 28 -
Density g/cm^ 0.948/ 0.957 ISO 1183
MFR190°/21.6 g/10min 6.2 ISO1133
MFR190°/5 g/10min 0.22 ISO1133
Notched Impact (23°c) mJ/mm2 24 ISO179/1eA
Hyd rostatic Strength (80 ° C) h 5000 (4.5 N/mm 12345) ISO1167
  •  Test speciment from compression moulded sheet at 23° C.
  • FRR values are statistical and calculated by dividing MFR values.
  • Test specimen from compressed moulded sheet 23 C sheet 23 ºC The data quoted are average values

Handling and Health Safety

Molten polymers could be injured skin or eye so safety glasses and appropriate gloves are suggested to prevent possible thermal injuries. Also appropriate ventilation is suggested in working by melt polymer. Accumulation of fines or dust particles that are in this grade is not suitable because of explosion hazard probability. So adequated filters and grounding exists at all time are recommended.

Storage

Polyethylene products (in pelletised or powder form) should not be stored in direct sunshine and/or heat radiation. Ultraviolet cause a change in the material properties.The Storage area should be dry and preferably don’t exceed 50 °C. it is advisable to process PE resine within 6 month after delivery. JPC would not ressponsible about quality diminishing such as color change, bad smell or ets which caused by bad storage conditions. It is better to process PE resin within 6 months after delivery.

packaging

Jam Polymers Polyolefin resins are supplied in Pellet form packed in 25kg bags. Alternative packaging modes are avalable for selected grades.

 

- On compression moulded according to ASTM D1928C Processing Conditions Recommended barrel tempratures range between 190 °C and 280 °C.

Shear-Viscosity @ 190 °C

HMcrp100n-pe100

 

The above values were Calculated from data for 100 µm produced on a 75mm Barrnage extruder with 190°C melt temperature using a 2:1 blow ratio and a gap die of 3.0 mm

  • black
  • 737.44KB
  • پی دی اف
  • PE100
  • 737.32KB
  • پی دی اف
امتیاز را وارد کنید
نام را وارد کنید
تعداد کاراکتر باقیمانده: 400
نظر خود را وارد کنید