General
|
|
|
|
|
|
Density
|
|
ISO 1183
|
g/cm3
|
1.04
|
|
Water Absorption
|
|
ASTM D 570
|
%
|
0.3
|
|
Rheological
|
|
|
|
|
|
Melt Flow Rate (MFR)
|
|
ISO 1133
|
g/10min
|
8
|
|
Mechanical
|
|
|
|
|
|
Tensile Strength
|
50 mm/min
|
ASTM D 638
|
MPa
|
27
|
|
Strain at break
|
50 mm/min
|
ASTM D 638
|
%
|
100
|
|
Flexural Strength
|
2 mm/min
|
ASTM D 790
|
MPa
|
40
|
|
Flexural Modulus
|
2 mm/min
|
ASTM D 790
|
MPa
|
1550
|
|
Izod Impact Strength Notched
|
+23°C - thickness 3.2 mm
|
ISO 180/4A
|
J/m
|
110
|
| |
0°C - thickness 3.2 mm
|
ISO 180/4A
|
J/m
|
90
|
| |
- 20°C - thickness 3.2 mm
|
ISO 180/4A
|
J/m
|
80
|
| |
- 40°C - thickness 3.2 mm
|
ISO 180/4A
|
J/m
|
75
|
| |
+23°C - thickness 4 mm
|
ISO 180/1A
|
kJ/m²
|
9.5
|
| |
- 40°C - thickness 4 mm
|
ISO 180/1A
|
kJ/m²
|
79
|
|
Charpy Impact Strength, Notched
|
+23°C
|
DIN 53453
|
kJ/m²
|
NB
|
|
Unnotched
|
+23°C
|
DIN 53453
|
kJ/m²
|
NB
|
|
Unnotched
|
- 40°C
|
DIN 53453
|
kJ/m²
|
R97
|
|
Rockwell Hardness
|
scale R
|
ISO 2039/2
|
kJ/m²
|
R103
|
|
Thermal
|
|
|
|
|
|
Vicat Softening Tempreture
|
10 N - 120°C/h
|
ISO 306/A120
|
ºC
|
106
|
| |
50 N - 120°C/h
|
ISO 306/B120
|
ºC
|
101
|
|
Deflection temp. under load (annealed)
|
1.8 MPa - 120°C/h
|
ASTM D 648
|
ºC
|
101
|
|
Ceofficient of linear thermal expansion
|
|
ASTM D 696
|
10 -5/ºC
|
9
|
|
Thermal Conductivity
|
|
ASTM C 177
|
W/(Km)
|
0.17
|
|
Moulding Shrinkage
|
|
ISO 294.4
|
%
|
0.4-0.6
|
|
Flammability
|
|
|
|
|
|
Flame behavior
|
thickness 1.5 mm
|
UL 94
|
class
|
HB
|
|
Glow wire test
|
thickness 3 mm
|
IEC 60695-2-1
|
ºC
|
650
|
|
Electrical
|
|
|
|
|
|
Surface resistivity
|
dry
|
IEC 60093
|
ohm
|
10+14
|
|
Volume resistivity
|
dry
|
IEC 60093
|
ohm*cm
|
10+15
|
|
Dielectric strength
|
dry
|
IEC 60243
|
kV/mm
|
30
|
|
Dielectric constant (relative permittivity)
|
1000 Hz - dry
|
IEC 60250
|
|
3.1
|
|
Dissipation factor
|
1000 Hz - dry
|
IEC 60250
|
|
15*10-³
|