14XF9

Loading

14XF9

14XF9

HDPE made via Spherilene Process

14XF9 is a HP-LLDPE blown film grade of excellent processability, good film strength combined with very good optical properties (transparency and gloss, and low level of gels). The additivation package of 14XF9 is particularly suitable for lamination.

HDPE: 14XF9
Features
  • good film strength combined
  • Excellent processability
  • very good optical properties(transparency and gloss, and low level of gels).
Density: 0.915
Applications
  • Film grade for lamination
MFI: 0.9
Additives
  • THERMAL ANOTIOXIDANT
  • ANTIBLOCKING AGENT

Material properties (This data are typical values and are not to be construed as product specifications)

Resin properties Unit Typical Value ASTM Method
Melt flow rate (190/2.16) (g/10’) 0.9 D 1238
Density (g/ml) 0.915 D 1505
Film properties @
Dart Impact (g) 110 D 1709
Elmendorf Tear (g) 130/480 D 1922
Tensile strenght at yield (MPa) 10.7/10.8 D 882
Tensile strenght at break (MPa) 40/35 D 882
Ultimate elongation (%) 680/760 D 882
2% Secant modulus (MPa) 190/210 D 882
Haze (%) 18 D 1003
Gloss 45° - 42 D 2457
@ On 25 R blown film extruded on a 25 mm extruder. BUR 2.5:1. Temperature profile 150 to 190°C; melt temperature 200 °C
Recommended processing conditions
Melt Temperature (°C) 190-240 -
Blow up ratio - 2.0-3.0 -
Die Gap (mm) 2.0-2.5 -
Thickness (micron) 18-180 -